Heat Treat Cycles: Difference between revisions
No edit summary |
No edit summary |
||
| Line 1: | Line 1: | ||
== ES Cycles == | == Easy Swage "ES" Cycles == | ||
=== ES-140 - Quench & Anneal Process === | === ES-140 - Quench & Anneal Process === | ||
| Line 27: | Line 27: | ||
=== <span style="color:red;">ES-202 - Controlled Stress Relief Procedure - Being Tested</span> === | === <span style="color:red;">ES-202 - Controlled Stress Relief Procedure - Being Tested</span> === | ||
Stress relief after work hardening or after machining, over 1" section thickness - Used on large buttons | Stress relief after work hardening or after machining, over 1" section thickness - Used on large buttons | ||
== Hardening "HS" Cycles == | |||
=== HS-300 - Quench & Temper for 8620 Steel === | |||
== Swager Die Hardening "SDCH" Cycles == | |||
=== SDCH-200 - Controlled Heat Treat Procedure to Harden S7 Tool Steel === | |||
Intended for hardening die material with 2"-5.999" sectional thickness | |||
== Hardware Heat Treat "MN" Cycles == | |||
=== MN-100 - Heat Treatment of AISI 1043-1045 to ASTM A194 Grade 2H Properties === | |||
Used for A194 hex nuts - carbon steel, alloy steel, and stainless steel - intended for high pressure or high temperature service | |||
Revision as of 11:57, 27 September 2023
Easy Swage "ES" Cycles
ES-140 - Quench & Anneal Process
Not currently in use
ES-150 - Spheroidize Anneal Process
Used to spheroidize anneal swage sockets
ES-160 - Controlled Anneal Process
Not in use anymore - Used to anneal Flemish Eye Sleeves before sub-zero cycle
ES-170 - Controlled Quench & Anneal Process
Not in use anymore - Used to quench & anneal Flemish Eye Sleeves before sub-zero cycle
ES-180 - Sub-Zero Quench & Sub-Critical Spheroidize Anneal
Used for Flemish Eye Sleeves, OCS Sleeves, large buttons, & Twist-On Buttons
ES-190 - Sub-Critical Spheroidize Anneal ("Sub-Zero" Process)
Used to anneal after work hardening or after machining - Used on Flemish Eye Sleeves, OCS Sleeves, & large buttons over 5/8" wall thickness or 1" wire rope size
ES-200 - Supplemental Annealing
Used to anneal after work hardening or after machining - Used on OCS Sleeves & large buttons
ES-201 - Controlled Stress Relief Procedure
Stress relief after work hardening or after machining, up to 1" section thickness - Used on OCS Sleeves
ES-202 - Controlled Stress Relief Procedure - Being Tested
Stress relief after work hardening or after machining, over 1" section thickness - Used on large buttons
Hardening "HS" Cycles
HS-300 - Quench & Temper for 8620 Steel
Swager Die Hardening "SDCH" Cycles
SDCH-200 - Controlled Heat Treat Procedure to Harden S7 Tool Steel
Intended for hardening die material with 2"-5.999" sectional thickness
Hardware Heat Treat "MN" Cycles
MN-100 - Heat Treatment of AISI 1043-1045 to ASTM A194 Grade 2H Properties
Used for A194 hex nuts - carbon steel, alloy steel, and stainless steel - intended for high pressure or high temperature service